ZrN是一种难熔硬质化合物，分解温度高，化学稳定性好，具有良好的耐高温、耐腐蚀、耐磨性能，是良好的高温结构材料、超硬工具材料及表面保护材料。
| 型号 | 平均粒度(D50) | 纯度(%) | 0(%) | H(%) | C(%) | N(%) | ||||
| ZrN3000 | 50-100nm | >99.0 | — | — | — | 10.5~13.3 | ||||
| ZrN0800 | 0.5-1.0um | >99.0 | ≤1.0 | ≤0.005 | ≤0.1 | 10.5~13.3 | ||||
| ZrN0020 | 1.0-3.0um | >99.5 | ≤.0.8 | ≤0.005 | ≤0.1 | 10.5~13.3 | ||||
| ZrN0021 | 1.0-3.0um (80%集中) |
>99.5 | ≤0.8 | ≤0.005 | ≤0.1 | 10.5~13.3 | ||||
| ZrNO003 | 10.0-50.0um | >99.9 | ≤0.5 | ≤0.005 | ≤0.1 | 10.5~13.3 | ||||
| ZrNO008 | -100+325mesh | >99.9 | ≤0.3 | ≤0.005 | ≤0.1 | 10.5~13.3 | ||||
| ZrNO001 | -200mesh | >99.99 | ≤0.1 | ≤0.005 | ≤0.001 | 10.5~13.3 | ||||
| 可根据客户需求进行定制化生产 | ||||||||||
| 元素 | 最大值 | 典型值 | 元素 | 最大值 | 典型值 | 元素 | 最大值 | 典型值 | ||
| Al | 0.0010 | 0.0005 | Fe | 0.0500 | 0.0300 | P | 0.0010 | 0.0005 | ||
| As | 0.0010 | 0.0005 | K | 0.0020 | 0.0010 | Pb | 0.0003 | 0.0001 | ||
| Bi | 0.0003 | 0.0001 | Mg | 0.0020 | 0.0010 | S | 0.0010 | 0.0005 | ||
| Ca | 0.0015 | 0.0006 | Mn | 0.0010 | 0.0005 | Sb | 0.0020 | 0.0010 | ||
| Cd | 0.0005 | 0.0001 | Mo | 0.0030 | 0.0015 | Si | 0.0050 | 0.0030 | ||
| Co | 0.0005 | 0.0001 | Na | 0.0020 | 0.0005 | Sn | 0.0003 | 0.0001 | ||
| Cr | 0.0050 | 0.0020 | Ni | 0.0050 | 0.0030 | Ti | 0.0050 | 0.0020 | ||
| Cu | 0.0003 | 0.0001 | Nb | 0.0030 | 0.0010 | V | 0.0050 | 0.0010 | ||